CERAWEAR material data sheet

Properties units values
Al2O3-content % ≥92
Hardness Mohs 9
Wear (ASTM C 704, 45⁰) cm3  max. 0,3
Bulk density g/cm3 3,65
Open porosity % 0
Compressive strength MPa 2600
Bending strength MPa 280
Vickers Hardness Hv 10 1100
Young’s Modulus GPa 300
Coefficient of linear expansion    
20 to 200°C x 10-6 / K 5 - 6
20 to 400°C   6 - 7
20 to 600°C   6 - 8
20 to 800°C   7 - 9,5
20 to 1000°C   7 - 8,5
Specific Heat J/kg*K 700 - 850
Water Absorption % 0
Thermal Conductivity (20-100°C) W/m*K 16 - 24
Electric strength KV/mm 10
Colour   white
Thermal shock resist ∆T°C 250
THE INFORMATION IN THIS DATA SHEET IS FOR DESIGN GUIDANCE ONLY. BAKONY DOES NOT WARRANTY THIS DATA AS ABSOLUTE VALUES. FORMING METHODS AND 
SPECIFIC GEOMETRY COULD AFFECT PROPERTIES.
News
Bakony Wear Tec. Ltd. continues his activity independently

Bakony Wear Tec. Ltd, the wear resistant specialist of the Bakony Group, continuous its activity - after 8 years co-operation with the Kalenborn group – 2013 in 100% Hungarian ownership and under the brand name CERAWEAR.

MORE
2013-04-19 09:39:54
 
1/1 
 


Bakony Wear Tec. Ltd.


  • H-8200 Veszprém
  • Csererdő, hrsz. 0104/2
  • Veszprém, H-8210
  • PO. Box 2078
  • HUNGARY

  • info@cerawear.hu
  • www.cerawear.hu
  • www.cerawear.eu

Contact us


  • Telephone
  • +36-88-563-480

  • Fax
  • +36-88-444-877

 

  • VAT number
  • 13555287-2-19 (HU13555287)

  • Bank (CIB Bank Zrt.)
  • Swift: CIBHHUHB (Veszprém Branch)
  • Bank account (HUF)
    HU66 11100300-13555287-01000003
  • Bank account (EUR)
    HU20 11100300-13555287-75000002